TI-200 Series (PPS-based) Gear TI grade

Share:


TI-200 Series (PPS-based) Gear TI grade

Injection Molded Products
Our Injection Molding Division provides precision machinery components and other small, complex products, as well as products with superior resistance to chemicals and wear.

TI-200 Series (PPS-based)

A Series with High Heat Resistance and Strength for Those Looking for a Low-Cost Option!
The TI-200 Series is based on PPS resin, which offers superior heat resistance and flame retardancy, strengthened with special fibers. Its favorable moldability lends itself well for manufacturing with reliably high accuracy. The combination of high-strength grade TI-250A and sliding grade TI-200C not only gives this series low self-abrasion, but it also lowers the abrasion with other materials under extreme usage conditions of high temperature and high torque.

Gear Grade Properties Table:

Property Testing Method Unit 250A 200C-H02 5013 5031
Specific gravity D792   1.67 1.67 1.40 1.45
Water absorption (24 Hrs) D570 % 0.02 0.02 0.33 0.28
Tensile strength D638 MPa 200 165 186 157
Tensile elasticity D638 % 2.3 1.9 15.0 8.0
Bending strength D790 MPa 260 210 235 196
Bending elasticity D790 GPa 12.7 10.5 4.9 6.4
Izod impact strength (notched) D256 J/m 130 105 127 59
Deflection temperature under load (1.82 MPa) D648 °C >260 >260 >278 >279
Fiber reinforcing     Reinforced
(PPS)
Reinforced
(PPS)
Non-reinforced
(PAI)
Non-reinforced
(PAI)
      High strength High strength
Wear resistance
Ultrahigh strength
Wear resistance
Ultrahigh strength
Wear resistance

* This is a table of representative examples based on values measured from testing carried out under specific conditions.