TI-200 Series (PPS-based) Gear TI grade
Brand: Toray Plastics Precision
Injection Molded Products
Our Injection Molding Division provides precision machinery components and other small, complex products, as well as products with superior resistance to chemicals and wear.
TI-200 Series (PPS-based)
A Series with High Heat Resistance and Strength for Those Looking for a Low-Cost Option!
The TI-200 Series is based on PPS resin, which offers superior heat resistance and flame retardancy, strengthened with special fibers. Its favorable moldability lends itself well for manufacturing with reliably high accuracy. The combination of high-strength grade TI-250A and sliding grade TI-200C not only gives this series low self-abrasion, but it also lowers the abrasion with other materials under extreme usage conditions of high temperature and high torque.
Gear Grade Properties Table:
Property | Testing Method | Unit | 250A | 200C-H02 | 5013 | 5031 |
---|---|---|---|---|---|---|
Specific gravity | D792 | 1.67 | 1.67 | 1.40 | 1.45 | |
Water absorption (24 Hrs) | D570 | % | 0.02 | 0.02 | 0.33 | 0.28 |
Tensile strength | D638 | MPa | 200 | 165 | 186 | 157 |
Tensile elasticity | D638 | % | 2.3 | 1.9 | 15.0 | 8.0 |
Bending strength | D790 | MPa | 260 | 210 | 235 | 196 |
Bending elasticity | D790 | GPa | 12.7 | 10.5 | 4.9 | 6.4 |
Izod impact strength (notched) | D256 | J/m | 130 | 105 | 127 | 59 |
Deflection temperature under load (1.82 MPa) | D648 | °C | >260 | >260 | >278 | >279 |
Fiber reinforcing | Reinforced (PPS) |
Reinforced (PPS) |
Non-reinforced (PAI) |
Non-reinforced (PAI) |
||
High strength | High strength Wear resistance |
Ultrahigh strength Wear resistance |
Ultrahigh strength Wear resistance |
* This is a table of representative examples based on values measured from testing carried out under specific conditions.